产品说明：
　　Intoductiont：
　　“束达”牌H200，F155玻纤绑扎带品质优良，它是由加捻无碱玻璃纤维和专用的耐高温热固化不饱和树
脂组成。
　　SHU DA H200, F155 banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin.
　　“束达”牌H200，F155玻纤绑扎带是利用从意大利Isola公司主套引进的技术和设备生产的。
　　SHU DA H200, Fl55 banding taPes are manufactured with the proprietory technology and advanced equipments which are transferred from VONROLL ISOLA of ITALY.
　　“束达”牌H200，F155玻纤绑扎带广泛用于交、直流电机，发电机和变压器，尤其是用于牵引电机。
　　SHU DA H200, F155 banding tapes are widely used in AC, DC motors, generators and transformers especially intraction motors.
　　规格
　　Specification
型号 type
宽度（mm）width
厚度（mm）thick ness
卷装形式 Put uP
H200－W
F155-W
10 15 20 25 30 50.60
± 10％
0.30
± 10％
盘状或筒状
spool or pancake

　　性能
　　Properties
H200－W
F155-W
耐热等级 Thermal class
H
F
挥发物含量 Volatile contenf
%
 不大于：
not above:2
树脂含量
Loss of weight at calcination
%
26±2
可溶性树脂含量
Soluble resin content
%
不小于：
above:90
固化前的抗拉强度
Tensile strength before curing
N/cm
不小于：
above:2000
 不小于：
above:1000*
最大绑扎张力
Maximum pull while banding
N/cm
1000
800
环行试样常态拉伸强度
Tensile strength of ringlike sample at room temperature after
curing
Mpa
20°C
不小于：
above:1000
不小于：
above:900*
环行试样热态拉伸强度
Tensile strength of ringlike sample at working temperature after curing
Mpa
200°C
155°C
不小于：
above:700
不小于：
above:560*
耐漏电起痕指纹
Proof tracking index
S
500V通过
above:500V
耐电弧 Are resistance
不小于：
above:160
平行层向击穿电压
Breakdown voltage Parallel to layers
KV
常态： 　　　　　　不小于：
normal condition　 above：25
经24小时浸水后： 　　不小于：
after soaked in　　　　　　　　　
water for 24 hours：　　above：10　
可固化性 Thermosetting
容易剥离和不粘连
OK
浸油后抗拉强度劣化率
Loss of tensile strength after soaked in oil
不大于：
not above: 10%